Abstract
Heterostructures of NiFe/NiO/[Co/Pt] with mutually orthogonal easy axes allow for isothermal tuning of the magnetic coercivity at room temperature with no associated shift in the hysteresis loop along the applied field axis. This is in contrast to what is typically seen in exchange biased heterostructures. The NiFe coercivity is enhanced from 14.5 to 105Oe through the application of moderate dc magnetic fields of
| Original language | English |
|---|---|
| Article number | 093901 |
| Journal | Journal of Applied Physics |
| Volume | 118 |
| Issue number | 9 |
| DOIs | |
| State | Published - Sep 7 2015 |
Fingerprint
All Science Journal Classification (ASJC) codes
- Physics and Astronomy(all)
Cite this
Isothermal tuning of magnetic coercivity in NiFe/NiO/[Co/Pt] heterostructures with orthogonal easy axes. / Baruth, Andrew.
In: Journal of Applied Physics, Vol. 118, No. 9, 093901, 07.09.2015.Research output: Contribution to journal › Article
}
TY - JOUR
T1 - Isothermal tuning of magnetic coercivity in NiFe/NiO/[Co/Pt] heterostructures with orthogonal easy axes
AU - Baruth, Andrew
PY - 2015/9/7
Y1 - 2015/9/7
N2 - Heterostructures of NiFe/NiO/[Co/Pt] with mutually orthogonal easy axes allow for isothermal tuning of the magnetic coercivity at room temperature with no associated shift in the hysteresis loop along the applied field axis. This is in contrast to what is typically seen in exchange biased heterostructures. The NiFe coercivity is enhanced from 14.5 to 105Oe through the application of moderate dc magnetic fields of
AB - Heterostructures of NiFe/NiO/[Co/Pt] with mutually orthogonal easy axes allow for isothermal tuning of the magnetic coercivity at room temperature with no associated shift in the hysteresis loop along the applied field axis. This is in contrast to what is typically seen in exchange biased heterostructures. The NiFe coercivity is enhanced from 14.5 to 105Oe through the application of moderate dc magnetic fields of
UR - http://www.scopus.com/inward/record.url?scp=84940848780&partnerID=8YFLogxK
UR - http://www.scopus.com/inward/citedby.url?scp=84940848780&partnerID=8YFLogxK
U2 - 10.1063/1.4929760
DO - 10.1063/1.4929760
M3 - Article
AN - SCOPUS:84940848780
VL - 118
JO - Journal of Applied Physics
JF - Journal of Applied Physics
SN - 0021-8979
IS - 9
M1 - 093901
ER -